性能項(xiàng)目 |
試驗(yàn)條件[狀態(tài)] |
測(cè)試方法 |
測(cè)試數(shù)據(jù) |
數(shù)據(jù)單位 |
|
|
物理性能 |
模收縮 |
|
|
1.7-1.9 |
% |
|
機(jī)械性能 |
破裂點(diǎn)拉伸變形量 |
100℃ |
ASTM D-638 |
>260 |
|
|
撓曲變形強(qiáng)度 |
23℃ |
ASTM D-790 |
103 |
MPa |
|
|
拉伸強(qiáng)度 |
122℃ |
ASTM D-638 |
26 |
MPa |
|
|
壓縮應(yīng)力 |
23℃,10%變形 |
ASTM D-695 |
106 |
MPa |
|
|
負(fù)載變形量 |
140kg/cm2,50℃ |
ASTM D-621 |
0.9 |
% |
|
|
IZOD沖擊試驗(yàn) |
23℃ |
ASTM D-256 |
59 |
j/m |
|
|
破裂點(diǎn)拉伸變形量 |
23℃ |
ASTM D-638 |
15 |
% |
|
|
抗剪強(qiáng)度 |
23℃ |
ASTM D-732 |
58 |
MPa |
|
|
破裂點(diǎn)拉伸變形量 |
122℃ |
ASTM D-638 |
>260 |
% |
|
|
撓曲系數(shù) |
23℃ |
ASTM D-790 |
3230 |
MPa |
|
|
破裂點(diǎn)拉伸變形量 |
-55℃ |
ASTM D-638 |
10 |
% |
|
|
撓曲系數(shù) |
100℃ |
ASTM D-790 |
1080 |
MPa |
|
|
拉伸強(qiáng)度 |
23℃ |
ASTM D-638 |
70 |
MPa |
|
|
洛氏硬度 |
|
ASTM D-785 |
107 |
R scale |
|
|
撓曲系數(shù) |
122℃ |
ASTM D-790 |
755 |
MPa |
|
|
拉伸強(qiáng)度 |
-55℃ |
ASTM D-638 |
103 |
MPa |
|
|
撓曲系數(shù) |
-55℃ |
ASTM D-790 |
4750 |
MPa |
|
|
撓曲系數(shù) |
70℃ |
ASTM D-790 |
1740 |
MPa |
|
|
拉伸強(qiáng)度 |
100℃ |
ASTM D-638 |
36 |
MPa |
|
|
拉伸強(qiáng)度 |
70℃ |
ASTM D-638 |
48 |
MPa |
|
|
壓縮應(yīng)力 |
23℃,1%變形 |
ASTM D-695 |
22 |
MPa |
|
|
IZOD沖擊試驗(yàn) |
缺口-40℃ |
ASTM D-256 |
52 |
j/m |
|
|
洛氏硬度 |
|
ASTM D-785 |
89 |
M scale |
|
|
熱性能 |
自燃性 |
|
UL-94 |
HB |
|
免責(zé)聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實(shí)性、準(zhǔn)確性和合法性由發(fā)布企業(yè)負(fù)責(zé)，環(huán)球塑化網(wǎng)對(duì)此不承擔(dān)任何保證責(zé)任。我們?cè)瓌t上建議您優(yōu)先選擇“塑企通”會(huì)員合作! （2）同時(shí)我們鄭重提醒各位買/賣家，交易前請(qǐng)?jiān)敿?xì)核實(shí)對(duì)方身份，切勿隨意打款或發(fā)貨，謹(jǐn)防上當(dāng)受騙。如發(fā)現(xiàn)虛假信息，請(qǐng)向環(huán)球塑化網(wǎng)舉報(bào)。